The angular contact bearing cage can bear both radial and axial loads. It can work at a high speed. The larger the contact Angle, the higher the axial bearing capacity. Contact Angle is 15 °, generally 20 °, 40 °.Widely used in machine tool spindle, high frequency motor, gas turbine, automobile, all kinds of transmission, compressor and other industries.
| Main material |
| Name of engineering plastics | Abbreviation code | Temperature range(ºC) |
| Glass fiber reinforced polyamide 66 | PA66-GF30 | -40-120 |
| PA66-GF25 | -40-120 |
| PA66-GF15 | -40-110 |
| PA66-GF10 | -40-110 |
| Polyamide 66 | PA66 | -40-90 |
| Glass fiber reinforced polyamide 46 | PA46-GF30 | -40-160 |
| PA46-GF25 | -40-150 |
| PA46-GF15 | -40-130 |
| Polyamide 46 | PA46 | -40-110 |
| Others | PI | >200 |
| PEEK |
| PAEK |
| PC | <100 |
| PP |
| PE |
| Main material property |
| Serial | Varieties | PA66-GF25 | PA66-GF30 | PA66-GF15 | PA66-GF10 | PA66 | PA46-GF30 | PA46-GF25 | PA46-GF15 | PA46 |
| 1 | Appearance | Fine grain, no obvious color difference, no coke particles. |
| 2 | melting point(ºC) | >255 | >295 |
| 3 | density(g/cm3) | 1.29~1.35 | 1.33~1.39 | 1.20~1.26 | 1.17~1.23 | 1.11~1.17 | 1.39~1.43 | 1.33~1.37 | 1.27~1.31 | 1.16~1.2 |
| 4 | Water absorbability(%) | <=1 | <=1 | <=1 | <=1.2 | <=1.5 | <=2.6 | <=2.8 | <=3.1 | <=3.7 |
| 5 | Glass fiber content(%) | 23~27 | 28~32 | 13~17 | 8~12 | - | 28~32 | 23~27 | 13~17 | - |
| 6 | tensile strength Mpa | >150 | >160 | >110 | >80 | >70 | >180 | >170 | >117 | >87 |
| 7 | impact strength (KJ/m2) | >42 | >50 | >35 | >28 | >60 | >80 | >70 | >50 | - |
| 8 | ball indentation hardness(MPa) | >200 | >210 | >170 | >160 | >130 | >220 | >205 | >190 | >170 |
| 9 | Bending spring modulus (Gpa) | >6 | >7 | >5 | >4 | >2.5 | >9 | >7.5 | >6 | >3 |
| 10 | Hot deformation temperature(1.8MPa)ºC | >240 | >240 | >240 | >220 | >70 | >290 | >280 | >275 | >190 |
| ps:Glass fiber is surface treated alkali free short glass fiber. |
Shipping Details
Samples by express like DHL. UPS .FedEx.TNT etc.
Goods by air cargo or by Sea.
Sample lead time: 1-2 days for stocked model. 5~10 days for customize samples.
Mass production time: 20-35 days for order.