Unidirectional bearing is a kind of bearing that can rotate freely in one direction and lock in the other direction. It is also called overrunning clutch. Widely used in textile machinery, printing machinery, automotive, home appliances and other fields. Engineering plastic cage is widely used.
| Main material |
| Name of engineering plastics | Abbreviation code | Temperature range(ºC) |
| Glass fiber reinforced polyamide 66 | PA66-GF30 | -40-120 |
| PA66-GF25 | -40-120 |
| PA66-GF15 | -40-110 |
| PA66-GF10 | -40-110 |
| Polyamide 66 | PA66 | -40-90 |
| Glass fiber reinforced polyamide 46 | PA46-GF30 | -40-160 |
| PA46-GF25 | -40-150 |
| PA46-GF15 | -40-130 |
| Polyamide 46 | PA46 | -40-110 |
| Others | PI | >200 |
| PEEK |
| PAEK |
| PC | <100 |
| PP |
| PE |
| Main material property |
| Serial | Varieties | PA66-GF25 | PA66-GF30 | PA66-GF15 | PA66-GF10 | PA66 | PA46-GF30 | PA46-GF25 | PA46-GF15 | PA46 |
| 1 | Appearance | Fine grain, no obvious color difference, no coke particles. |
| 2 | melting point(ºC) | >255 | >295 |
| 3 | density(g/cm3) | 1.29~1.35 | 1.33~1.39 | 1.20~1.26 | 1.17~1.23 | 1.11~1.17 | 1.39~1.43 | 1.33~1.37 | 1.27~1.31 | 1.16~1.2 |
| 4 | Water absorbability(%) | <=1 | <=1 | <=1 | <=1.2 | <=1.5 | <=2.6 | <=2.8 | <=3.1 | <=3.7 |
| 5 | Glass fiber content(%) | 23~27 | 28~32 | 13~17 | 8~12 | - | 28~32 | 23~27 | 13~17 | - |
| 6 | tensile strength Mpa | >150 | >160 | >110 | >80 | >70 | >180 | >170 | >117 | >87 |
| 7 | impact strength (KJ/m2) | >42 | >50 | >35 | >28 | >60 | >80 | >70 | >50 | - |
| 8 | ball indentation hardness(MPa) | >200 | >210 | >170 | >160 | >130 | >220 | >205 | >190 | >170 |
| 9 | Bending spring modulus (Gpa) | >6 | >7 | >5 | >4 | >2.5 | >9 | >7.5 | >6 | >3 |
| 10 | Hot deformation temperature(1.8MPa)ºC | >240 | >240 | >240 | >220 | >70 | >290 | >280 | >275 | >190 |
| ps:Glass fiber is surface treated alkali free short glass fiber. |
Shipping Details
Samples by express like DHL. UPS .FedEx.TNT etc.
Goods by air cargo or by Sea.
Sample lead time: 1-2 days for stocked model. 5~10 days for customize samples.
Mass production time: 20-35 days for order.