The thrust needle roller bearing is provided with a shaping cage. It can reliably fix and guide a large number of needle rollers, so that these needle rollers can withstand heavier axial load and impact load. And it takes up less space. Widely used in various fields, especially in the field of power tools.
| Main material |
| Name of engineering plastics | Abbreviation code | Temperature range(ºC) |
| Glass fiber reinforced polyamide 66 | PA66-GF30 | -40-120 |
| PA66-GF25 | -40-120 |
| PA66-GF15 | -40-110 |
| PA66-GF10 | -40-110 |
| Polyamide 66 | PA66 | -40-90 |
| Glass fiber reinforced polyamide 46 | PA46-GF30 | -40-160 |
| PA46-GF25 | -40-150 |
| PA46-GF15 | -40-130 |
| Polyamide 46 | PA46 | -40-110 |
| Others | PI | >200 |
| PEEK |
| PAEK |
| PC | <100 |
| PP |
| PE |
| Main material property |
| Serial | Varieties | PA66-GF25 | PA66-GF30 | PA66-GF15 | PA66-GF10 | PA66 | PA46-GF30 | PA46-GF25 | PA46-GF15 | PA46 |
| 1 | Appearance | Fine grain, no obvious color difference, no coke particles. |
| 2 | melting point(ºC) | >255 | >295 |
| 3 | density(g/cm3) | 1.29~1.35 | 1.33~1.39 | 1.20~1.26 | 1.17~1.23 | 1.11~1.17 | 1.39~1.43 | 1.33~1.37 | 1.27~1.31 | 1.16~1.2 |
| 4 | Water absorbability(%) | <=1 | <=1 | <=1 | <=1.2 | <=1.5 | <=2.6 | <=2.8 | <=3.1 | <=3.7 |
| 5 | Glass fiber content(%) | 23~27 | 28~32 | 13~17 | 8~12 | - | 28~32 | 23~27 | 13~17 | - |
| 6 | tensile strength Mpa | >150 | >160 | >110 | >80 | >70 | >180 | >170 | >117 | >87 |
| 7 | impact strength (KJ/m2) | >42 | >50 | >35 | >28 | >60 | >80 | >70 | >50 | - |
| 8 | ball indentation hardness(MPa) | >200 | >210 | >170 | >160 | >130 | >220 | >205 | >190 | >170 |
| 9 | Bending spring modulus (Gpa) | >6 | >7 | >5 | >4 | >2.5 | >9 | >7.5 | >6 | >3 |
| 10 | Hot deformation temperature(1.8MPa)ºC | >240 | >240 | >240 | >220 | >70 | >290 | >280 | >275 | >190 |
| ps:Glass fiber is surface treated alkali free short glass fiber. |
Shipping Details
Samples by express like DHL. UPS .FedEx.TNT etc.
Goods by air cargo or by Sea.
Sample lead time: 1-2 days for stocked model. 5~10 days for customize samples.
Mass production time: 20-35 days for order.